The effects of TiO2 nanotubes on bond strength and radiopacity of a self-adhesive resin cement in self-curing mode / Os efeitos de nanotubos de TiO2 na resistência de união e radiopacidade de um cimento resinoso auto-adesivo no modo auto-polimerizável

Objective: The aim of this in vitro study w as t o analyze the influence of the titanium dioxide nanotubes i n a self-cure mode polymerization of a dual resin luting agent through push out bond strength and radiopacity tests. Material and Methods: After mixed with a commercial du al self-adhesive resin cement, three concentrations o f tit anium dioxide nanotubes (0.3, 0.6, and 0.9% by weight) we re analyzed in self-curing mode. T he bond strength to bovine root dentin and fi berglass posts was assessed with the push out bond str ength t est and was evaluated in three thirds (cervical, middle and apical) (n=10), followed by failure mode analysis (SEM), and the ISO standard 9917-2 was followed for radiopacity test (n=10). Data were statistically analyzed by one-way ANOVA test, followed by Tukey's test (α=0.05). Results: Reinforced self-adhesive resin cement with 0.6% titanium dioxide nanotubes showed significant difference compared to the control gr oup for push out test (p=0.00158). The modified groups did not s how significant difference among thirds (p=0.782). Radiopacity sh owed higher value for group w ith 0.9% titanium dioxide nanotubes in comparison w ith control group (p<0.001). Conclusion: The addition of titanium dioxide nanotubes to a self-adhesive resin cement increased the bond strength to dentin and radiopacity values in the self-cure polymerization mode (AU)

Objetivo: O objetivo deste estudo in vitro foi analisar a influência de nanotubos de dióxido de titânio na polimerização química de um agente cimentante resinoso dual através de testes de resistência à união e radiopacidade. Material e Métodos: Após misturado com um cimento resinoso auto-adesivo comercial, três concentrações de nanotubos de dióxido de titânio (0,3, 0,6 e 0,9% em peso) foram analisadas. A resistência da união para a dentina da raiz bovina e os pinos de fibra de vidro foi avaliada pelo teste de push-out e avaliada em três terços (cervical, médio e apical) (n = 10), seguido pelo análise de modo de falha (MEV) e a norma ISO 9917-2 foi seguido para teste de radiopacidade (n = 10). Os dados foram analisados estatisticamente pelo teste ANOVA um fator seguido do teste de Tukey (α = 0,05). Resultados: O cimento resinoso auto-adesivo reforçado com nanotubos de dióxido de titânio a 0,6% mostrou diferença significativa em comparação com o grupo controle para teste de push-out (p=0,00158). Os grupos modificados não mostraram diferença significativa entre os terços (p=0,782). A radiopacidade mostrou maior valor para o grupo com nanotubos de dióxido de titânio 0,9% em comparação com o grupo controle (p<0,001). Conclusão: A adição de nanotubos de dióxido de titânio a um cimento resinoso auto-adesivo aumentou a os valores de resistência de união à dentina e radiopacidade no modo de polimerização química do agente cimentante (AU)

A new approach for Y-TZP surface treatment: evaluations of roughness and bond strength to resin cemen

Abstract Objective This study aims to evaluate the effect of sonochemical treatment on the surface of yttria-stabilized tetragonal zirconia (Y-TZP) before and after the final sintering. Material and Methods Twenty-eight Y-TZP discs were divided into four groups (n=7), according to surface treatment: PRE: pre-sintering sonication with 30% nominal power for 15 min; POS: post-sintering sonication with 30% nominal power for 15 min; JAT: air abrasion with 50-μm alumina particles; and CON: control group with no treatment. The POS and JAT groups were sintered before sonication and the PRE group after sonication. Surface roughness was analyzed using confocal microscopy, after which resin cement cylinders were placed on the surface of the Y-TZP discs and subjected to mechanical microshear bond strength test until fracture. Surface roughness and microshear bond strength values underwent ANOVA and the Tukey tests. Results The surface roughness values for the PRE group (299.91 nm) and the POS group (291.23 nm) were not significantly different (p≥0.05), statistically, and the surface roughness value of the JAT group (925.21 nm) was higher than those of PRE and POS (p=0.007) groups. The mechanical microshear bond strength test showed that there was no statistically significant difference between the groups (p=0.08). Conclusions Therefore, the results showed that sonochemical treatment modifies the Y-TZP surface and is similar to the well-established sandblasting surface treatment regarding the strength of the bond with the resin cement.

Marginal adaptation in proximal cavities restored with composites and other materials / Adaptação marginal em cavidades proximais com compósitos e outros materiais

Objective: To evaluate the marginal adaptation, in enamel (E) and dentin (D), of composite resin (CR) associated with flowable resin composite (flow), bulk fill flowable base (bulk) and resin modified glass ionomer cement (RMGIC) in slot cavities. Material and Methods: The study was conducted after approval (Protocol No. 21148413.4.0000.5417) from Ethics Committee. Forty extracted human molar teeth were randomly assigned in eight experimental groups: E-CR, E-BULK, E-FLOW, E-RMGIC, D-CR, D-BULK, D-FLOW, D-RMGIC. The occlusal surface was planned, two slot cavities with standard sizes (depth: 2.0 mm, height: 2.5 mm, width: 2.0 mm) were created on a machine for making cavities. The teeth were restored and after 24h subjected to 2000 cyclic loading and sectioned for analysis of marginal adaptation by scanning electron microscopy (SEM). The micrographs were analyzed with the Image J program to measure the size of marginal gaps. The data were transformed into percentages (%GAPS = LG ÷ LM × 100) and analyzed by 2-way ANOVA followed by the post hoc Tukey test (α=0.05). Results: There was a significant difference between different treatments (p0.05). Conclusions: It was concluded that restorations with flowable composite resin and bulk fill liners exhibit the same behavior, but the RMGIC liner increased marginal gap (AU)

Objetivo: Avaliar a adaptação marginal, em esmalte (E) e dentina (D), de restaurações com resina composta (RC) associada a resina composta fluida (flow), resina bulk fill (bulk) e cimento de ionômero modificado por resina (CIVMR) em cavidades tipo slot. Materiais e Métodos: O estudo foi realizado após aprovação no Comitê de Ética e Pesquisa (Protocolo no. 21148413.4.0000.5417). Quarenta molares humanos foram aleatoriamente distribuídos em oito grupos experimentais: E-RC, E-BULK, E-FLOW, E-CIVMR, D-RC, D-BULK, D-FLOW, D-CIVMR. A superfície oclusal foi planificada e duas cavidades tipo slot com tamanhos padronizados (profundidade: 2,0 mm, altura: 2,5 mm, largura: 2,0 mm) foram realizadas em uma máquina para confecção de cavidades. Os dentes foram restaurados e, após 24h, submetidos a 2000 ciclos mecânicos e foram seccionados para análise da adaptação marginal em microscopia eletrônica de varredura (MEV). As micrografias foram analisadas através do programa Image J para medir as fendas marginais. Os dados foram transformados em porcentagens (%fendas = largura da fenda / largura da margem x 100) e analisados através do teste ANOVA-2 critérios seguido do teste de Tukey (α=0,05). Resultados: Houve diferença significante entre os diferentes tratamentos (p0,05). Conclusões: Concluiu-se que as restaurações com base de resina flow e bulk fill exibiram o mesmo comportamento, mas a base de CIVMR aumentou a fenda marginal. (AU)

Curing depth of a silorane-based resin composite

Introduction: The silorane-based resin appears aiming to minimize the effects of polymerization shrinkage, but other properties must be studied. Objective: To evaluate the polymerization depth of two composites with different organic matrix. Material and methods: 80 cylindrical specimens were prepared using a metallic matrix, with three layers (top, middle and bottom), 1 mm high and 5 mm in diameter. The specimens were divided into eight groups (n = 10) according to the composite resins: Filtek P90 (3M/ESPE); Filtek Z250 (3M/ESPE), light-cured with a LED device with different irradiance and times (600mW/cm2 x 40s, 1000mW/cm2 x 40s, 1000mW/cm2 x 20s; 1400mW/cm2 x 20s). The irradiance was controlled by placing plastic rings coupled to the device's tip. Immediately after polymerization, the specimens' layers were separated and five Knoop microhardness readings (initial hardness) were performed on each one of the four layers (0, 1, 2, and 3 mm). After 7 day storage in water at 37ºC, new readings were performed (final microhardness). The data were analyzed by four-way ANOVA (resin, energy density, depth and time) and Tukey test (α = 0.05). Results: The microhardness decreased with the depth increasing both in the initial and 7 day readings. The hardness increased with the highest power densities. The resin P90 had lower hardness values. Conclusion: The silorane-based resin showed Knoop microhardness values significant smaller than those of methacrylate-based resin in almost all evaluated parameters. However, both presented similar behaviors in relation to the curing depth.

Teleducation about Cleft Lip and Palate: An Interdisciplinary Approach in the Promotion of Health

Introduction The Young Doctor Project (YDP) uses Telehealth and Interactive Teleducation instruments to promote the integration of different areas of health and to build knowledge. This methodology can also foster public awareness on various issues related to health. In this context, the objective of this study was to emphasize cleft lip and palate (CLP), which is one of the most common birth defects in Brazil. Objective The study aimed to apply a model of education regarding CLP, based on the dynamics of the YDP, and to evaluate the participants' knowledge acquired after participating in the YDP. Methods The participants were 41 students, 13 to 15 years of age and at the eight- and ninth-grade levels in a private elementary school in Bauru (Brazil). To analyze the performance of the participants, a questionnaire was administered before and after the completion of the training program. The training program was structured in three steps using: (1) interactive teleducation classes, (2) a cybertutor, and (3) practical activities. Results There was a statistically significant difference between the pre- and postparticipation questionnaire results. The improved performance of participants is evidenced by the increase in the rate of correct answers on all issues. Conclusion The YDP on CLP was applied in the school setting following the three steps recommended by the project, and, after the implementation of the training program, there was a significant increase in participants' knowledge of CLP. The YDP on CLP proved an effective tool in promoting health education. .

Effect of sealants in the composite surface roughness after tooth brushing / Efeito de selantes na rugosidade de resinas compostas após a escovação simulada

This in vitro study evaluated the influence of 4 surface sealers on the surface roughness of composite resins. Fifty specimens were divided into 10 groups, as follows: G1. (Control 1) Concept resin; G2. Concept + Fortify; G3. Concept + Biscover; G4. Concept + Lasting Touch; G5. Concept + Fill Glaze; G6. (Control 2) Esthet X; G7. Esthet X + Fortify; G8. Esthet X + Biscover; G9. Esthet X + Lasting Touch; G10. Esthet X + Fill Glaze. Specimens (15mm in length, 4 mm in depth and 5 mm in width) were made using a matrix and were stored in distilled water at 37ºC for 24 hours. After storage, specimens were polished using 320, 600 abrasive SiC paper under running water and the initial roughness was measured using a perfilometer. Surface sealers were applied and a new measurement of roughness was made. Specimens were submitted to 100,000 cycles of abrasive dentifrice brushing followed by another surface roughness measurement. Qualitative analysis was made by using SEM. Results were submitted to 3-way modified ANOVA (p<0.05) and Tukey's test. Results: Surface sealant provided smoother surfaces for both tested composite resins (G2=0.0727, G3=0.0147, G4=0.0307, G5=0.0253, G7=0.0173, G8=0.0333, G9=0.0480, G10=0,0480). After the abrasion test, the control group presented lower roughness surface (G1=0.0600, G6=0.1007). No statistical difference were found between Fortify (G2=0.0740, G7=0.0673) and Biscover (G7=0.0440). Lasting Touch presented rougher surfaces in relation to the other groups (G4= 0.1253, G9=0.0980), followed by Fill Glaze (G5=0.0933, G10= 0.0847). The application of surface sealant did not provide roughness optimization after tooth brushing simulation for the 2 composite resins tested.

Este estudo avaliou, in vitro, a influência de 4 selantes de superfície na rugosidade de duas resinas compostas. Cinqüenta espécimes foram confeccionados e divididos em 10 grupos com 5 espécimes cada, em função da combinação entre resina composta e selante de superfície, sendo: G1. Controle Concept; G2. Concept + Fortify; G3. Concept + Biscover; G4. Concept + Lasting Touch; G5. Concept + Fill Glaze; G6. Controle Esthet X; G7. Esthet X + Fortify; G8. Esthet X + Biscover; G9. Esthet X + Lasting Touch; G10. Esthet X + Fill Glaze. Os espécimes (15mm X 4 mm X 5 mm) foram confeccionados e armazenados em água destilada à 37ºC por 24 horas. Após este período, os espécimes foram planificados com lixas de granulometria 320, 600 e a rugosidade inicial foi aferida. Aplicaram-se os selantes de superfície e uma nova aferição da rugosidade superficial foi realizada. Os espécimes foram submetidos a 100.000 ciclos de escovação, seguido de nova mensuração da rugosidade. Os resultados foram submetidos aos testes ANOVA a 3 critérios e Tukey. A aplicação do selante de superfície diminuiu a rugosidade superficial das resinas compostas testadas (G2=0,0727, G3=0,0147, G4=0,0307, G5=0,0253, G6=0,0960, G7=0,0173, G8=0,0333, G9=0,0480). Nenhuma diferença estatística foi encontrada entre o grupo Fortify (G2=0,0740, G7=0,0673) e Biscover (G7=0,0440). Os maiores valores de rugosidade foram apresentados pelo grupo Lasting Touch (G4= 0,1253, G9=0,0980), seguido do Fill Glaze (G5=0,0933, G10= 0,0847). A aplicação do selante de superfície não otimizou a rugosidade das duas resinas compostas testadas após o teste de abrasão simulada.

Avaliação da resistência de união de reparos de resina composta, utilizando-se diferentes tratamentos de superfície / Evaluation of microtensile bond strength of composite resin repair using different surface treatments

Objetivo: Avaliar a resistência de união de reparos de restaurações em resina composta utilizando-se diferentes tratamentos de superfície. Materiais e Métodos: Foram utilizadas 180 amostras de resina composta Tetric Ceram® (Ivoclar/Vivadent), distribuídas em 9 grupos (n=20/grupo). No momento do reparo, cada grupo recebeu tratamento de superfície específico: ácido fosfórico a 37% (Ivoclar/Vivadent); ácido hidrofluorídrico a 10% (Dentsply) ou microjateamento com partículas de óxido de alumínio de 50μm (Micro Jato VH®). Em seguida, aplicou-se o sistema adesivo Heliobond® (Ivoclar/Vivadent), associado ou não ao agente silanizadorMonobond-S® (Ivoclar/Vivadent). Foram também confeccionados espécimes que não sofreram nenhum tipo de reparo (grupo controle). Os espécimes ficaram armazenados em água deionizada por 18 meses. Posteriormente cada amostra foi submetida ao teste de resistência de união à microtração em máquina de ensaio universal (EMIC DL500BF), a uma velocidade de 0,5 mm/minuto. Os dados obtidos em MPa foram submetidos a avaliação da normalidade da variável microtração por meio do teste Kolmogorov-Smirnov. Considerando quea variável não apresentou distribuição normal (p<0,001) foram realizados os testes de Kruskal-Wallis e Mann-Whitney. O valor de p considerado foi menor que 0,05, exceto, quando se utilizou da correção de Bonferroni(p<0,00138). Resultados: Os espécimes do grupo controle apresentaram resistência à tração estatisticamente superior em relação aos demais grupos. O emprego do ácido fosfórico e posterior inserção do sistema adesivo apresentou resultados estatisticamente significante em relação aos demais grupos reparados. Conclusões: A resistência coesiva da resina composta foi superior às outras técnicas de reparo utilizadas. O emprego do ácido fosfórico e posterior inserção do sistema adesivo demonstrou ser o tratamento ideal para o reparo derestaurações em resina composta.

Técnica mista: clareamento dentário e microabrasão: relato de caso clínico / Mixed technique: tooth bleaching and microabrasion: clinical xase report

O objetivo deste trabalho é apresentar a resolução estética do caso clínico de um paciente com dentes escuros e manchas de fluorose, em que foi realizado o clareamento dentário em consultório, associado à microabrasão do esmalte. O clareamento foi efetuado nos dentes de ambas as arcadas, exceto nos molares. Após condicionamento do esmalte, o agente clareador à base de peróxido de hidrogênio a 35 por cento (Lase Peroxide Sensy, DMC Equipamentos Ltda.) foi aplicado e ativado duas vezes de 3 minutos com aparelho de luz híbrida de LED/laser de diodo terapêutico (Whitening Lase II, DMC Equipamentos Ltda.). Esse processo foi repetido cinco vezes, na mesma sessão, seguido de polimento, laserterapia e aplicação do gel dessensibilizante por 4 minutos. Em uma segunda sessão de clareamento, os caninos e pré-molares receberam mais duas aplicações do gel clareador ativado com luz híbrida. Ao final do procedimento, o paciente ainda apresentava manchas brancas nos dentes superiores, sendo realizada, no final da sessão, a microabrasão do esmalte. Ao final do tratamento, pode-se constatar resultado estético satisfatório alcançado por meio do clareamento dos dentes e remoção das manchas hipocalcificadas.

The objective of this paper was to present the esthetics resolution of a clinical case of a patient with discolored teeth and fluorosis which performed in-office tooth whitening plus enamel microabrasion. Bleaching was done in the teeth of both arches, except the molars. After etching enamel with phosphoric acid at 37% for 15 seconds, the whitening agent with 35% of hydrogen peroxide (Lase Peroxide Sensy, DMC Equipamentos Ltda) was applied twice and activated for three minutes with a hybrid LED/Laser light appliance (Whitening Lase II, DMC Equipamentos Ltda). This process was repeated five times in the same session, followed by polishing, laser therapy and application of desensitizing gel for 4 minutes. In a second session of bleaching, canines and premolars received two more applications of the whitening gel activated with hybrid light. At the end of the procedure, the patient still had white spots on the upper teeth, being held at the end of the session, the microabrasion of the enamel. At the end of treatment, one can see satisfactory final result achieved by means of teeth whitening and removal of hipocalcified stains

Glass ionomer cements and their role in the restoration of non-carious cervical lesions

Glass ionomer based materials are clinically popular in several areas of restorative dentistry, but restoration of cervical lesions has proven particularly successful. Various etiologies, conformations, locations and structural characteristics make non-carious cervical lesions more challenging to adhesive restorative procedures and marginal seal in the long run. Due to their characteristics, glass ionomer cements (GICs) have precise indication for these cases. Moreover, the use of a GIC base underneath composite resin, the so-called "sandwich" or mixed technique, allows associating the good characteristics of composite resins and GICs, and has been considered quite useful in the restoration of non-carious cervical defects. The aim of this paper is to critically review the literature and discuss peculiar features of GICs regarding their role in the restoration of non-carious cervical lesions.

Water sorption and solubility of different calcium hydroxide cements

OBJECTIVES: Calcium hydroxide cements have been largely used in deep cavities due to their abilities to stimulate dentin formation. However, their resistance can be relatively low and their solubility relatively high, in many instances. This study evaluated water sorption and solubility of different calcium hydroxide cements, in order to show alterations that may reduce their effectiveness. MATERIAL AND METHODS: Five discs (20 mm in diameter and 1.5 mm thick) of three different materials (Biocal®, Dycal® and Hidro C®) were prepared with the aid of a ring-shaped metallic matrix. After being stored at 37ºC for 24 h, the discs were weighed on a precision weight scale, dehydrated and weighed again. Immediately after weighing, discs were stored for a week in 50 mL of distilled water at 37ºC and, then, weighed again, dehydrated and submitted to a new weighing. The loss of soluble material and its water sorption was obtained from the difference between the initial and the final dry mass of each disc, after 1 week of immersion in water. Data were analyzed for significant differences by two-way ANOVA and Tukey's test (p<0.05). RESULTS: Mean water sorption values (g) ± standard deviation and percentage ( percent), for each evaluated cement, were: Biocal® (0.006 ± 0.001 / 2.15); Dycal® (0.016 ± 0.004 / 5.49); and Hidro C® (0.025 ± 0.003 / 8.27). Mean solubility values (g) ± standard deviation and percentage ( percent), for each evaluated cement, were: Biocal® (0.002 ± 0.001 / 0.72); Dycal® (0.013 ± 0.004 / 4.21); and Hidro C® (0.023 ± 0.004 / 7.65). CONCLUSIONS: Biocal® absorbed less water and was less soluble than the other evaluated cements; Hidro C® exhibited the highest water sorption and solubility values; and there were significant differences among all evaluated experimental groups.

Restauração estética em dente posteriores: relato de caso / Esthetic restoration of posterior tooth with composite resin: case report

A realizações de restaurações estéticas de resina composta tem sido amplamente difundida na prática odontológica atual. Com o aperfeiçoamento dos sisitemas adesivos e das resinas compostas, é possível realizar preparos cada vez menos invasivos, com segurança quanto às suas aplicações e indicações. Restaurações de resina composta em dentes posteriores têm apresentado resultados satisfatórios de resistência e longevidade, uma vez que apresentam propriedades mecânicas aprimoradas. Dessa forma, este artigo tem como objetivo demonstrar e discutir os principais fatores relacionados à confecção de uma restauração de resina composta em dentes posteriores por meio da substituição insatisfatória, abordando os aspectos de contração de polimerização das resinas e formas de minimizar seus danos.

Resistência à remoção de braquetes ortodônticos sob ação de diferentes cargas contínuas / Shear bond strength of orthodontic brackets using different static loading application

OBJETIVO: testar se existe alteração na resistência adesiva de dois cimentos utilizados na colagem de acessórios ortodônticos ao esmalte dentário bovino, sendo um de polimerização química (Concise ortodôntico) e outro fotopolimerizável (Transbond XT), após a aplicação de cargas contínuas. METODOLOGIA: foram utilizados para este estudo 80 dentes bovinos e 80 braquetes metálicos. O esmalte bovino foi condicionado com ácido fosfórico a 37 por cento por 1 minuto e depois lavado e seco. A aplicação dos adesivos, manipulação e aplicação dos dois cimentos foram feitas de acordo com as instruções dos fabricantes. Após 24 horas, todos os braquetes foram submetidos a cargas contínuas de 30g, 70g e 120g, menos o grupo controle, que não recebeu carga alguma. Os espécimes ficaram imersos em água filtrada por 28 dias dentro de uma estufa a 37ºC. Depois deste período, as amostras foram submetidas a testes de cisalhamento em uma Máquina de Ensaios Universal Kratos. Os resultados foram registrados e enviados para análise estatística. CONCLUSÕES: (1) o cimento Concise apresentou maior resistência à remoção que o cimento Transbond XT para todas as cargas utilizadas, (2) não houve diferença estatisticamente significante na resistência adesiva frente às três cargas utilizadas para os dois cimentos testados; (3) no momento da fratura, conforme ocorreu o aumento da carga, a porcentagem de fratura do esmalte diminuiu para o Concise, ao contrário do cimento Transbond XT, onde a porcentagem de fratura de esmalte se manteve constante com o aumento das cargas.

AIM: The purpose of this study was to test differences on bond strength between auto-cured (Concise) and light-cured (Transbond XT) cements after static loading and shear test. METHODS: Eighty bovine teeth and metallic orthodontic brackets (Morelli Ortodontia Braquete Edgewise/Rickets) were tested after static loads of 30, 70 and 120grs. Bovine enamel was conditioned with 37 percent phosphoric acid gel for one minute, rinsed and dried. Adhesives were applied and brackets were bonded according to manufacturer's instructions. Cement thickness was standardized with the use of a heavier Gilmore needle. After 24 hours, half of the specimens were submitted to the static loads of 30, 70 and 120grs. Control group remained unloaded. Then, specimens were immersed in distilled water for 28 days at 37ºC. Afterwards, orthodontic brackets were attached to a loop wire and submitted to a shear force (Máquina de Ensaios Kratos Universal Kratos) under a crosshead speed of 0.5mm/min and load cell of 500Kgf. A two-way ANOVA test (alpha = 0.05) was used to detect significant interactions between cements and static loads. CONCLUSIONS: (1) The Concise cement showed more statistically significant bond strength values than the Transbond XT cement for all static loads; (2) No statistically significant differences were observed regarding static loads for all cements tested and (3) Higher static loads provided less enamel fracture in the Concise group after shear test, whereas in the Transbond XT the rate of enamel fracture remained unchanged regardless of previous load applied.

Volumetric polymerization shrinkage of contemporary composite resins

The polymerization shrinkage of composite resins may affect negatively the clinical outcome of the restoration. Extensive research has been carried out to develop new formulations of composite resins in order to provide good handling characteristics and some dimensional stability during polymerization. The purpose of this study was to analyze, in vitro, the magnitude of the volumetric polymerization shrinkage of 7 contemporary composite resins (Definite, Suprafill, SureFil, Filtek Z250, Fill Magic, Alert, and Solitaire) to determine whether there are differences among these materials. The tests were conducted with precision of 0.1 mg. The volumetric shrinkage was measured by hydrostatic weighing before and after polymerization and calculated by known mathematical equations. One-way ANOVA (ß=0.05) was used to determine statistically significant differences in volumetric shrinkage among the tested composite resins. Suprafill (1.87±0.01) and Definite (1.89±0.01) shrank significantly less than the other composite resins. SureFil (2.01±0.06), Filtek Z250 (1.99±0.03), and Fill Magic (2.02±0.02) presented intermediate levels of polymerization shrinkage. Alert and Solitaire presented the highest degree of polymerization shrinkage. Knowing the polymerization shrinkage rates of the commercially available composite resins, the dentist would be able to choose between using composite resins with lower polymerization shrinkage rates or adopting technical or operational procedures to minimize the adverse effects deriving from resin contraction during light-activation.

Resistência de união de um cimento resinoso a diferentes superfícies de alumina densamente sinterizada / Shear bond strength of a resin cement to different surfaces of densely sintered alumina

O propósito deste estudo foi avaliar a resistência adesiva ao cisalhamento de um cimento resinoso à alumina densamente sinterizada, testando o tratamento superficial feito pelo fabricante. O cimento utilizado foi o Multilink (Ivoclar - Vivadent) e a alumina foi a Procera® Alumina (Nobel Biocare) constituída por 99,9% de óxido de alumínio densamente sinterizado. Trinta e dois cilindros de alumina foram confeccionados pela Nobel Biocare, onde um dos extremos deste cilindro recebeu o tratamento superficial e o outro não. Para a aplicação do cimento resinoso sobre os cilindros de alumina, utilizou-se uma matriz de Teflon com um orifício central de 3,5mm de diâmetro e 3mm de profundidade. Foram determinados 4 grupos experimentais: Grupo 1- superfície sem tratamento; Grupo 2 - superfície sem tratamento e com aplicação de adesivo; Grupo 3 - superfície com o tratamento realizado pelo fabricante; Grupo 4 - superfície com tratamento realizado pelo fabricante e com adesivo. Após a aplicação do cimento nos 4 grupos, os espécimes foram armazendos em água deionizada a 37°C durante 24h, sendo, em seguida, montados em uma máquina universal de ensaios para realização dos testes de resistência ao cisalhamento. Os resultados foram submetidos à análise de variância a dois critérios e ao teste de Tukey para comparação entre os grupos. A superfície tratada (grupo 3)apresentou valores significativamente maiores que todos os outros grupos. A presença do adesivo diminuiu a resistência adesiva nas duas superfícies, embora não houvesse diferença significante quando aplicado na superfície sem tratamento.

Influência da textura superficial dos implantes / Texture of the titanium implant surfaces

Dentre as várias características dos implantes a topografia da superfície é reconhecida como fator capaz de alterar a resposta das células dos tecidos adjacentes modificando a migração, inserção, proliferação e síntese de colágeno no local, determinando assim o tipo de tecido que será obtido na interface osso-implante e sua integração. Graças aos diferentes tipos de tratamentos tornou-se possível obter várias formas de caracterização da superfície facilitando a compreensão dos padrões de formação óssea, comportamento das células e até mesmo prever o tipo cicatricial que será obtido a partir da conformação dos tecidos adjacentes às superfícies dos implantes. Superfície de titânio com a rugosidade e microestrutura complexa aumenta a osseointegração no contato osso e implante, eleva a força de torque de remoção in vivo e a diferenciação in vitro dos osteoblastos induzidos pela função de rugosidade e topografia na osseointegração. Em superfícies de implantes tratadas com plasma de titânio (TPS), jateadas com areia e tratadas com ácido (SLA) os resultados demonstraram que tanto a rugosidade como o tratamento químico das superfícies pode influenciar bastante a força superficial de cisalhamento (resistência oferecida à remoção). Estas características da superfície do titânio, além de otimizar o procedimento, podem ainda, por exemplo, permitir a colocação dos implantes em função mais precocemente e ampliar a gama de aplicações possíveis para osso alveolar de densidade inferior ou favorecer sua aplicação em osso regenerado.

Effect of a metal primer on the bond strength of the resin-metal interface

Para avaliar o efeito de diferentes tratamentos superficiais sobre a resistência ao cisalhamento da união entre uma liga metálica (Co-Cr-Mo - Remanium CD) e um cimento resinoso (Rely XTM) e analisar o tipo de fratura durante a separação dos espécimes, quarenta pares de discos metálicos foram fundidos, regularizados e polidos, submetidos a quatro ciclos térmicos (vácuo, 960ºC, 8 minutos) e divididos aleatoriamente em quatro grupos. Cada grupo recebeu um tipo de tratamento: Grupo PSP: Polimento com lixa d'água Nº 600; Grupo PCP: Polimento com lixa 600 e aplicação do condicionador metálico Alloy Primer (Kuraray); Grupo JSP: Jato de óxido de alumínio de 100µm, e Grupo JCP: Jato de óxido de alumínio de 100mm, e aplicação do Alloy Primer. Os grupos foram cimentados e armazenados em água destilada a 37ºC por 36 horas e submetidos ao ensaio de resistência ao cisalhamento. A média e o desvio padrão (em kgf/cm2) obtidos para cada grupo foram: PSP 4,0/0,4; PCP 88,9/33,6; JSP 163,2/27,6; JCP 144,5/54,0. Após a análise estatística os autores concluíram que: os maiores valores foram produzidos pelos grupos jateados (JSP, JCP), independentemente da aplicação do primer; o Alloy Primer aumentou a retentividade entre o cimento Rely X e a superfície polida da liga de Co-Cr-Mo, entretanto sua força de união não superou a alcançada através do jateamento; todos os espécimes apresentaram falha adesiva na interface testada.

Utilização do cobalto-cromo na confecção de infraestruturas de prótese implantossuportadas / The use of cobalt-chromium alloy for confection of frameworks for implant-supported prostheses

Os autores aprensentam uma revisão de literatura sobre a utilização da liga de cobalto-cromo na confecção e subestruturas de próteses sobre implantes, relacionando suas características físicas e biológicas com as necessidades encontradas para a elaboração de subestruturas de próteses implantossuportadas e constatando a viabilidade desta utilização

Amálgama: mais de 160 anos de serviços prestados à Odontologia / Amalgam: more than 160 years of good services performed to Dentistry

Os autores discorrem a respeito do amálgama desde as primeiras evidências de sua utilizaçäo na Odontologia, seu desenvolvimento ao longo dos anos e seus aspectos atuais

Influência da termociclagem na análise da resistência ao cisalhamento do cimento de ionômero de vidro (Fuji Ortho Lc) e da resina composta (Concise Ortodôntico) utilizados na colagem de bráquetes ortodônticos / Thermocycling influence on the analysis of bonding dental of orthodontic brackets cemented with composite resin (Concise Ortodontico) and glass ionomer cement (Fuji Ortho LC)

A pesquisa teve como objetivo analisar a resistência ao cisalhamento da resina composta (CONCISE 3M do Brasil Ltda) e cimento de ionômero de vidro (Fuji Ortho LC - GC Corporation, Tokyo, Japan) utilizados na colagem de braquetes ortodônticos (Abzil Lancer) em coroas de dentes bovinos. Os dentes foram recolhidos e armazenados em soluçäo de cloramina T a 1 por cento, e após serem limpos, tiveram suas raízes incluídas em resina epóxica. Foram utilizados 20 dentes, sendo 10 para cada material. A colagem dos braquetes foi realizada seguindo instruçöes recomendadas pelo fabricante de cada material, tendo sido previamente estabelecida a profilaxia com pedra pomes e água, utilizando taça de borracha girando em baixa rotaçäo. Os corpos de prova ficaram armazenados em estufa a 37 graus C por 24 horas. Terminado esse tempo, 5 corpos de prova de cada grupo foram submetidos à termociclagem (300 ciclos de 15 segundos cada - 5 graus C e 55 graus C) e os restantes permaneceram em estufa. Terminada a termociclagem, os corpos de prova retornaram ao armazenamento até perfazer um total de 8 dias para todos os dentes dos dois grupos. O teste de cisalhamento foi realizado para os diferentes espécimes em Máquina de Ensaio Universal (KRATOS, velocidade de 0,5mm/minuto). Os resultados foram analisados estatisticamente, o que permitiu verificar uma diferença estatisticamente significante entre os dois materiais, sendo que a resina composta CONCISE mostrou maior resistência de uniäo do que o cimento de ionômero de vidro Fuji Ortho LC